Može li se Inconel 600 zavariti?
Inconel-hemijski sastav
| Inconel | Ni | Cr | Fe | Mo | Nb | Co | Mn | Cu | Al | Ti | Si | C | S | P | B |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 600 | 72 | 14.0-17.0 | 6.0-10.0 | 1 | 0.5 | 0.5 | 0.15 | 0.015 | |||||||
| 617 | 44.2-56.0 | 20.0-24.0 | 3 | 8.0-10.0 | 10.0-15.0 | 0.5 | 0.5 | 0.8-1.5 | 0.6 | 0.5 | 0.15 | 0.015 | 0.015 | 0.006 | |
| 625 | 58 | 20.0-23.0 | 5 | 8.0-10.0 | 3.15-4.15 | 1 | 0.5 | 0.4 | 0.4 | 0.5 | 0.1 | 0.015 | 0.015 | ||
| 690 | 59.5 | 30 | 9.2 | 0.35 | 0.01 | 0.02 | 0.35 | 0.019 | 0.003 | ||||||
| 718 | 50.0-55.0 | 17.0-21.0 | balans | 2.8-3.3 | 4.75-5.5 | 1 | 0.35 | 0.2-0.8 | 0.65-1.15 | 0.3 | 0.35 | 0.08 | 0.015 | 0.015 | 0.006 |
| X-750 | 70 | 14.0-17.0 | 5.0-9.0 | 0.7-1.2 | 1 | 1 | 0.5 | 0.4-1.0 | 2.25-2.75 | 0.5 | 0.08 | 0.01 |
Svojstva zavarivanja Inconela 600
Inconel 600 zavarivanje općenito ne zahtijeva predgrijavanje. Međutim, kada je temperatura osnovnog metala niža od 15 stepeni, područje spoja dužine od 250 mm do 300 mm sa obe strane treba prethodno zagrejati na 15 do 20 stepeni da bi se izbegle pore usled kondenzacije vlage. Kako bi se spriječio rast zrna i taloženje karbida, međuprolazna temperatura ne bi trebala biti viša od 100 stepeni. Treba paziti da se spriječi brzo hlađenje, koje može rezultirati poroznošću. Područje zavarivanja treba pažljivo očistiti prije zavarivanja.